PolyWood™

Basic

This Specialty family provides unique filaments from Polymaker to unlock new 3D printing applications.

PolyWood™

PolyWood™ features Polymaker's Jam-Free™ technology and Polymaker's Stabilized Foaming™ technology:

Jam-Free™ technology improves the heat stability of Polymaker’s PLA filaments with softening temperatures over 140 °C. As a result, Polymaker’s PLA filaments show minimal softening in the “cold end” and can melt rapidly once entering the heating zone, leading to excellent printing quality with zero risk of nozzle jams.

PolyWood™ is a wood mimic filament without actual wood powder, which removes all risks of nozzle clogs. PolyWood™ is made entirely with PLA using a special foaming technology. It exhibits the same density and appearance as wood. Stabilized Foaming™ technology is used to produce foamed filaments, whose foam structure can survive the printing process and be inherited by the printed parts. This enables light weight 3D printed parts with unprecedented surface finish.

Basic Materials Data

Nozzle Temperature:
190˚C – 210˚C

Printing Speed:
30mm/s – 50mm/s

Bed Temperature:
25˚C – 60˚C

Bed Surface:
almost any surface with a thin coat of Nano Adhesive

Cooling Fan:
ON

Printing Setting

Young’s Modulus:
2636 ± 330 Mpa

Tensile Strength:
23.2 ± 0.4 Mpa

Bending Strength:
52.9 ± 0.3 Mpa

Charpy Impact Strength:
2.1 ± 0.2 kJ/m2

Mechanic Properties

Glass Transition Temperature:
62˚C

Vicat Softening Temperature:
60˚C

Melting Temperature:
151˚C

Thermal Properties