LUVOCOM® 3F PAHT CF 9891 BK

About The Materials 

LUVOCOM 3F PAHT CF 9891 BK is a 15% carbon fiber reinforced PA6 filament that is engineered for quality controlled 3D printing of end-use parts that require high strength, stiffness and temperature resistance.

Materials Documentations

LUVOCOM® 3F PAHT CF 9891 BK

LUVOCOM® 3F PAHT CF 9891 BK is a 15% carbon fiber reinforced material. LUVOCOM® 3F PAHT CF 9891 BK is a material from LEHVOSS. It is designed for industrial applications, easy to print with low warping an increased layer adhesion. LUVOCOM® 3F PAHT CF 9891 BK is a PA6 based material, it has a low influence from moisture and temperature on dimensional stability and electrical properties.


Features:

  • Lehvoss Luvocom 3F PAHT CF 9891 BK inside

  • 15% carbon fiber reinforced PA6 filament for improved stiffness

  • 50% reduced water uptake at a four times slower rate compared to other PA6 filaments

  • Temperature resistant up to 160 °C (200h)

  • Tensile strength up to 120 MPa

  • 3D prints with high dimensional accuracy and increased layer adhesion

  • Good electrical properties


Packaging

LUVOCOM® 3F PAHT CF 9891 BK is available on carton spools, repacked under quality control of Lehmann&Voss&Co


Additional information

Recommended temperature for heated bed is 65-75˚C. Adhesion is possible on different surfaces. LUVOCOM® 3F PAHT CF 9891 BK can be used on all common desktop FDM technology or FFF 3D printers. Dry the spool before printing: 12 hours at 70°C or 4 hours at 100°C. *Please consider the use of a hardened steel nozzle when printing with LUVOCOM® 3F PAHT CF 9891 BK. The carbon fibers are abrasive and will result in fast wear of regular brass nozzles.


Storage

Cool and dry (15-25˚C) and away from UV light. This enhances the shelf life significantly.


Applications

Materials Informations

Weight:

Diameter:

Colour:

500g, 750g

1.75mm, 2.85mm

Black